OEM HT200 HT250 Ductile Cast Iron Green Sand Castings Process

My dear friend, the goods received are good and hope we can work together for more items.

—— Angelo

Yu-Long company is indeed professional in casting field, and help to improve the design and save the cost for us. Thanks very much.

—— John

The delivery is on time, and cooperation is happy.

—— Christopher

I'm Online Chat Now

OEM HT200 HT250 Ductile Cast Iron Green Sand Castings Process

OEM HT200 HT250 Ductile Cast Iron Green Sand Castings Process
OEM HT200 HT250 Ductile Cast Iron Green Sand Castings Process

Large Image :  OEM HT200 HT250 Ductile Cast Iron Green Sand Castings Process

Product Details:

Place of Origin: China
Brand Name: non-standard
Certification: ISO9001;TS16949
Model Number: custom-built

Payment & Shipping Terms:

Minimum Order Quantity: 1 Ton
Price: quote according to drawing technical requirements
Packaging Details: Plywood crate + VCI Anti-Rust Bag
Delivery Time: within 60 days
Payment Terms: T/T, L/C
Supply Ability: 300 Tons every month
Detailed Product Description
Material: HT200 HT250 Process: Green Sand Casting Process
Machining: CNC Machining Surface: Shot Blasting
Heat Treatment: Annealed Name: Ductile Cast Iron
High Light:

HT250 Ductile Cast Iron

,

HT200 Ductile Cast Iron

,

HT200 green sand casting

OEM HT200 HT250 Ductile Cast Iron Green Sand Castings Process

 

Ductile Cast Iron Application

 

Metal Parts Solution for Vehicle, Agriculture machine, Construction Machine, transportation equipment, Valve and Pump system, Agriculture machine metal Parts, engine bracket, truck chassis bracket, gear box , gear housing , gear cover, shaft, spline shaft , pulley, flange, connection pipe, pipe, hydraulic valve , valve housing ,Fitting , flange, wheel, fly wheel, oil pump housing, starter housing, coolant pump housing, transmission shaft , transmission gear, sprocket, chains etc.

 

Ductile Cast Iron Description and Process
 
1.Ductile Casing EN-GJS-400-18 Spheroidal Cast Iron Material OEM Castings Company
 
2. Production process:

    green sand castings process,

    pre-coated sand  castings process;

    resin sand castings process

    we can produce iron castings from 50 gram to 2000 kilograms
 
3. Machining process: CNC machine, machining center, lathe, mill machine, drill machine, etc.
 
4. Surface treatment process: paint coating, electrophoretic coating, electrogalvanizing coating, black oxide coating, phosphate coating, powder coating, etc.
 

 

What is in Ductile Iron? (Composition)

If you were to do a chemical analysis of ductile iron, this is what you would normally find:
Iron ~94%
Carbon 3.2 – 3.60%
Silicon 2.2 – 2.8%
Manganese 0.1 – 0.2%
Magnesium 0.03 – 0.04%
Phosphorus 0.005 – 0.04%
Sulfur 0.005 – 0.02%
Copper <= 0.40%
To improve the strength of ductile iron, additional tin or copper can be added. To improve corrosion resistance, copper, nickel, or chromium can replace anywhere from 15-30% of the iron.
 
Ductile Iron Grade Chart
ASTM A536 1993 (USA)

 

Grade Tensile Strength
σ≥/Mpa
Yield Strength
σ≥/Mpa
Elongation
δ≥(%)
ANSI/ASTM UNS
60-40-18 F32800 414 276 18
65-45-12 F33100 448 310 12
80-55-06 F33800 552 379 6.0
100-70-03 F34800 689 483 3.0
120-90-02 F36200 827 621 2.0
Special Purpose      
60-42-10   415 290 10
70-50-05   485 345 5.0
80-60-03   555 415 3.0

 
 

GB/T 1348 1998 (China)

 

Grade

Tensile strength

σb≥/MPa

Yield strength

σ0.2≥/MPa

Elongation

δ5≥(%)

Hardness

HBS

QT400-18

QT400-18-LT*

400 250 18 130~180
QT400-15 400 250 15 130~180
QT450-10 450 310 10 160~210
QT500-7 500 320 7 170~230
QT600-3 600 370 3 190~270
QT700-2 700 420 2 225~305
QT800-2 800 480 2 245~335
QT900-2 900 600 2 280~360

 

Low temperature V notch impact tested (-20±2℃)

 

EN 1563 1997 (European Standard)

Grade Tensile Strength
σ≥/Mpa
Yield Strength
σ≥/Mpa
Elongation
δ≥(%)
Symbol Number
EN GJS 350-22 EN JS1010 350 220 22
EN GJS 350-22-LT* EN JS1015 350 220 22
EN GJS 400-18 EN JS1020 400 250 18
EN GJS 400-18-LT* EN JS1025 400 240 18
EN GJS 400-15 EN JS1030 400 250 15
EN GJS 450-10 EN JS1040 450 310 10
EN GJS 500-7 EN JS1050 500 320 7
EN GJS 600-3 EN JS1060 600 370 3
EN GJS 700-2 EN JS1070 700 420 2
EN GJS 800-2 EN JS1080 800 480 2
EN GJS 900-2 EN JS1090 900 600 2

Low temperature V notch impact tested (-20±2℃)

 

Common Ductile Iron Grades
 
While there are many different ductile iron specifications, foundries routinely offer 3 common grades;

 

Physical and Mechanical Properties ASTM A536, Grade 60-40-18 ASTM A536, Grade 65-45-12 ASTM A536, Grade 80-55-06
Tensile Strength, min, psi 60,000 65,000 80,000
Tensile Strength, min, MPa 414 448 552
Yield Strength, min, psi 40,000 45,000 55,000
Yield Strength, min, MPa 276 310 379
Elongation in 2 in. or 50 mm, min % 18 12 6
Density lb/in3 0.256 0.256 0.256
Density g/cm3 7.1 7.1 7.1
Melting Temperature (Degrees F) 2,100 – 2,190 2,100 – 2,190 2,100 – 2,190
Melting Temperature (Degrees C) 1,150 - 1,200 1,150 - 1,200 1,150 - 1,200
Compressive Strength Ksi 429 429 429
Compressive Strength MPa 2960 2960 2960
UNS F32800 F33100 F33800